Article
Group / Description
Curing Method
Chemical type
Final strength
Fixture time
Article:
 MK 1122
Group / Description
thread locker , low strength

for securing and sealing of screw and threaded connections
AM:
anaerobic

Viscosity/mPa⋅s:
200
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
5 - 15 minutes
Article:
 MK 1131
Group / Description
thread locker , low strength

for securing of screws, sealing of threaded and pipe connections
AM:
anaerobic

Viscosity/mPa⋅s:
1000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
5 - 25 minutes
Article:
 MK 1222
Group / Description
thread locker , medium strength

for securing and sealing of screw and threaded connections
AM:
anaerobic

Viscosity/mPa⋅s:
200
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
2 - 10 minutes
Article:
 MK 1226
Group / Description
thread locker , medium strength

for securing and sealing of screw and threaded connections
AM:
anaerobic

Viscosity/mPa⋅s:
600 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
2 - 10 minutes
Article:
 MK 1231
Group / Description
thread locker , medium strength

securing of screws, sealing of threaded and screw connections
AM:
anaerobic

Viscosity/mPa⋅s:
1000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
2 - 10 minutes
Article:
 MK 1231T
Group / Description
thread locker , medium strength

AM:
anaerobic

Viscosity/mPa⋅s:
1.000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
2 - 20 minutes
Article:
 MK 1232
Group / Description
thread locker , medium strength

for securing and sealing of passive and inactive surfaces without the use of an activator
AM:
anaerobic

Viscosity/mPa⋅s:
1.000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
8 hours
Handfestigkeit:
2 - 6 minutes
Article:
 MK 1312
Group / Description
thread locker , high strength

hard to disassemble, very low viscous, good capillary action, also suitable for subsequent application and waterproofing of grey cast iron
AM:
anaerobic

Viscosity/mPa⋅s:
12
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
8 hours
Handfestigkeit:
2 - 10 minutes
Article:
 MK 1325
Group / Description
thread locker , high strength

high strength, low viscous thread locking and sealing
AM:
anaerobic

Viscosity/mPa⋅s:
500
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
8 hours
Handfestigkeit:
2 - 10 minutes
Article:
 MK 1326
Group / Description
thread locker , high strength

for securing and sealing of inactive and passive surfaces without the use of an activator
AM:
anaerobic

Viscosity/mPa⋅s:
500
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
8 hours
Handfestigkeit:
2 - 6 minutes
Article:
 MK 1331
Group / Description
thread locker , high strength

thread locking and sealing, hard to disassemble
AM:
anaerobic

Viscosity/mPa⋅s:
1000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
2 - 10 minutes
Article:
 MK 1523
Group / Description
thread locker , high strength

thread locker, low viscous, hard to disassemble, for bonding of adherend, temperature resistant up to 220°C (long term exposure)
AM:
anaerobic

Viscosity/mPa⋅s:
300
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
5 - 15 minutes
Article:
 MK 1531
Group / Description
thread locker , high strength

medium viscous threadlocker for all thread sizes, hard to disassemble, temperature resistant up to 220°C (constant exposure)
AM:
anaerobic

Viscosity/mPa⋅s:
1000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
5 - 15 minutes
Article:
 MK 1812
Group / Description
anaerobic/UV-lightcuring , high strength

low viscous, capillary, for subsequent bonding
AM:
anaerobic/lightcuring

Viscosity/mPa⋅s:
12
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
10 hours
Handfestigkeit:
5 - 15 minutes (anaerobic), 20 - 40 seconds (light)
Article:
 MK 2138
Group / Description
pipe sealing , low strength

high viscous, for all thread sizes
AM:
anaerobic

Viscosity/mPa⋅s:
8000
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
5 - 15 minutes
Article:
 MK 2235
Group / Description
pipe sealing , medium strength

high viscous, KTW-Reg. C 1078/00/st
AM:
anaerobic

Viscosity/mPa⋅s:
5000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
2 - 10 minutes
Article:
 MK 2236
Group / Description
pipe sealing , medium strength

sealing of threaded and pipe connections on passive and inactive surfaces even without the use of an activator
AM:
anaerobic

Viscosity/mPa⋅s:
5.000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
8 hours
Handfestigkeit:
2 - 6 minutes
Article:
 MK 2238
Group / Description
pipe sealing , medium strength

high viscous
AM:
anaerobic

Viscosity/mPa⋅s:
8000
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
5 - 15 minutes
Article:
 MK 2241
Group / Description
pipe sealing , medium strength

high viscous, liquid Teflon®, for all thread sizes, white
AM:
anaerobic

Viscosity/mPa⋅s:
10 000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
5 - 10 minutes
Article:
 MK 2255
Group / Description
pipe sealing , medium strength

high viscous, for all thread sizes, DVGW-certified
AM:
anaerobic

Viscosity/mPa⋅s:
500 000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
2 - 10 minutes
Article:
 MK 2332
Group / Description
pipe sealing , high strength

flexible pipe sealing for metat/metal, metal/synthetics, synthetics/synthetics
AM:
anaerobic

Viscosity/mPa⋅s:
2000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
3 - 10 minutes
Article:
 MK 2336
Group / Description
pipe sealing , high strength

for securing and sealing of threaded and pipe connections with passive and inactive surfaces even without the use of an activator
AM:
anaerobic

Viscosity/mPa⋅s:
5.000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
8 hours
Handfestigkeit:
2 - 6 minutes
Article:
 MK 2338
Group / Description
pipe sealing , high strength

pipe- and surface sealing, hard to disassemble, field of hydraulics, DVGW approved - up to 65 bar pressure
AM:
anaerobic

Viscosity/mPa⋅s:
8000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
8 hours
Handfestigkeit:
3 - 10 minutes
Article:
 MK 2535
Group / Description
pipe sealing

High viscosity product recommended especially for pipe threads exposed to heat
AM:
anaerobic

Viscosity/mPa⋅s:
4.000 thix
Chem. Basis:
Di-Methacrylatester
Endfestigkeit:
24 Stunden
Handfestigkeit:
5 - 15 Minuten
Article:
 MK 3147
Group / Description
surface sealing , low strength

pasty, run-resistant, for sealing of flanges, easy to detach
AM:
anaerobic

Viscosity/mPa⋅s:
70 000 pasty
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
5 - 15 minutes
Article:
 MK 3247
Group / Description
surface sealing , medium strength

pasty, run-resistant, for sealing of flanges, detachable
AM:
anaerobic

Viscosity/mPa⋅s:
70 000 pasty
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
10 hours
Handfestigkeit:
2 - 15 minutes
Article:
 MK 4422
Group / Description
joining , high strength

extremely fast cure, highest strength, temperature resistant
AM:
anaerobic

Viscosity/mPa⋅s:
200
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
8 hours
Handfestigkeit:
1 - 7 minutes
Article:
 MK 4423
Group / Description
joining , high strength

for fastening of bearings, extremely fast cure, super high strength, temperature resistant, not classified
AM:
anaerobic

Viscosity/mPa⋅s:
200
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
12 hours
Handfestigkeit:
3 - 10 minutes
Article:
 MK 4425
Group / Description
joining , high strength

fast cure even on passive surfaces
AM:
anaerobic

Viscosity/mPa⋅s:
500
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
6 hours
Handfestigkeit:
1 - 7 minutes
Article:
 MK 4433
Group / Description
joining , high strength

high viscous, extreme strength, DVGW-certified
AM:
anaerobic

Viscosity/mPa⋅s:
3000
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
6 hours
Handfestigkeit:
1 - 7 minutes
Article:
 MK 4451
Group / Description
joining , high strength

for the repair of blowholes and cracks on worn-out bearings, bushings and hub- shaft connections
AM:
anaerobic

Viscosity/mPa⋅s:
50.000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
24 hours
Handfestigkeit:
3 - 10 minutes
Article:
 MK-4825
Group / Description
anaerobic/UV-lightcuring , high strength

low viscous, anaerobic and light curing
AM:
anaerobic/lightcuring

Viscosity/mPa⋅s:
500
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
3 hours
Handfestigkeit:
5 - 15 minutes (anaerobic), 20 - 40 seconds (light)
Article:
 MK-4838
Group / Description
anaerobic/UV-lightcuring , high strength

high viscous, gap filling
AM:
anaerobic/lightcuring

Viscosity/mPa⋅s:
8000 thix
Chem. Basis:
di-methacrylate-ester
Endfestigkeit:
10 hours
Handfestigkeit:
5 - 15 min. (anaerobic), 20 - 40 sec. (light)