| low viscous, extremely fast cure, high strength, temperature resistant | |
| Strength class: | high strength |
| Curing system: | humidity |
| Viscosity: | 40 |
| Chemical type: | modified methyl-cyanoacrylate |
| Final Strength: | 20 hours |
| Fixture Time: | 2 - 4 seconds |
| Appearance: |  |
BEST-CA 114 is a one-component, solvent free cyanoacrylate adhesive based on methyl-cyanoacrylate.
BEST-CA 114 is a universal product for bonding of plastics, e.g. polyamide, PVC, PMMA and various elastomeres amongst each other and especially for bonding of metals. It is of low viscosity and therefore designed for applications with small adhesive gap. The good capillary action/effect allows a subsequent application.
BEST-CA 114 is very fast cure. After full cure the adhesive is high strength and temperature resistant.
BEST-CA 114 is ready-to-use and can be applied from the original container.
BEST-CA 114 is applied spot-wise or bead like. Assemble parts by using short, firm pressure. Curing process starts within seconds. On most materials fixture time is reached within 3 to 5 seconds. 85 % of final cure is reached after 30 minutes, 100% after 20 hours. The rate of cure depends on the ambient relative humidity. A relative humidity of 40 to 60% will lead to best results. Lower values may delay cure.
Bonding surfaces must be dry, free of dust and grease as well as other contaminants. Sand-blasting, grinding and staining bonding surfaces will enhance adhesion on bonding surfaces.
CHEMICAL AND ENVIRONMENTAL RESISTANCE
BEST-CA adhesives show good resistance to changing climatic conditions and chemical influences.
product inquiry for a sample to CA 114
Only for commercial customers and for serial production.
Klicken Sie auf den unteren Button, um den Inhalt von zu laden.
Only for commercial customers and for serial production.
Klicken Sie auf den unteren Button, um den Inhalt von zu laden.
Safety data sheet only available via email
Klicken Sie auf den unteren Button, um den Inhalt von zu laden.